FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 |
1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.28 g/cm3 |
| Melt flow index (MFI) | ISO 1133-1 (@225°C – 2.16 kg) | 6.5 - 10 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 | 78 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 10 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 0°/0° |
| Nozzle Temperature | 250°C |
| Bed T° | 85 - 90°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/1A/50 | 7,773.3 MPa |
| Tensile Strength | ISO 527-2/1A/50 | 92.9 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 1.9 % | |
| Tensile Stress at Break | ISO 527-2/1A/50 | 92.9 MPa | |
| Tensile strain at break (type A) | ISO 527-2/1A/50 | 1,9 % | |
| Flexural modulus | ISO 178 | 5,664 MPa | |
| Deformation at Flexural Strain | ISO 178 | 4.2 % | |
| Flexural strength* | ISO 178 | 138 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 120.6 MPa | |
| Flexural stress at break | ISO 178 | 42.2 MPa | |
| Deformation at Flexural Strength | ISO 178 | 3.1 % | |
| Charpy impact resistance | ISO 179-1/1eA | 4.6 kJ/m² | |
| Shore Hardness | ISO 868 | 78,8D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |
Created on 13/08/2018 - Revised on 13/03/2023.